What is the difference between hot rolled and plate?

When steel is heated up the molecules align in to what they called a matrix. This becomes a stronger steel. In cold rolling they start with a huge billet of steel and run it throguh rollers compressing the steel. In cold roll steel youll have the same matrix as you did in the original billet (for the most part its really less change to the matrix). Cold rolling also uses many more rollers and or passes to get the stock to the final size and shape this is why it will tend to have a nicer looking finish.

With hot rolled steel the matrix will change become more dense and well aligned. In stock removal this is a good thing as it will grind and file etc smoother for us (more consitancy) than cold rolled. In the end though if your heat treating is good other than the ease of finishing both will end up the same or very close to the same in hardness grain structure etc.

Remember on raw hot rolled youll need to remove a portion of the mettal from top bottom and both esdges to get past the scale layer.

OT sort of but intresting. You know that alluminum foil you use to wrap your lunch in? Well it is a multi layer or damascus alloy. To get foil they use hot roller to thin out a very huge billet of aluminum. Once its at a given thickness it is folded in half and ran through the rollers again to increase its strength. Depending on how heavy a duty its to be used for it may be folded again and again ran through the rollers. So you heavy duty foil is folded twice giving a 4 layer damscus aluminum foil

Just a fun little fact i picked up watchign how its made heheh

Ok this was just on history channel and a while back how its made.When steel is heated up the molecules align in to what they called a matrix. This becomes a stronger steel. In cold rolling they start with a huge billet of steel and run it throguh rollers compressing the steel. In cold roll steel youll have the same matrix as you did in the original billet (for the most part its really less change to the matrix). Cold rolling also uses many more rollers and or passes to get the stock to the final size and shape this is why it will tend to have a nicer looking finish.With hot rolled steel the matrix will change become more dense and well aligned. In stock removal this is a good thing as it will grind and file etc smoother for us (more consitancy) than cold rolled. In the end though if your heat treating is good other than the ease of finishing both will end up the same or very close to the same in hardness grain structure etc.Remember on raw hot rolled youll need to remove a portion of the mettal from top bottom and both esdges to get past the scale layer.OT sort of but intresting. You know that alluminum foil you use to wrap your lunch in? Well it is a multi layer or damascus alloy. To get foil they use hot roller to thin out a very huge billet of aluminum. Once its at a given thickness it is folded in half and ran through the rollers again to increase its strength. Depending on how heavy a duty its to be used for it may be folded again and again ran through the rollers. So you heavy duty foil is folded twice giving a 4 layer damscus aluminum foilJust a fun little fact i picked up watchign how its made heheh

An Overview of Hot Rolled Steel

Click to Enlarge

Hot rolled steel is steel that has undergone the rolling process at a temperature above its recrystallization temperature (usually 1700° F or greater). Compared to unprocessed steel, the processed material exhibits greater formability and workability, making it easier to work with in subsequent processing operations.

The hot rolling process starts with a large, rectangular slab of metal referred to as a billet. First, the billet is heated and compressed into a large roll. While still hot, it passes through a series of rotating rollers to achieve the desired dimensions. In sheet metal production operations, the rolled steel is then wound into coiled rolls and left to cool. In production operations involving other forms, the processed material is cut into the specified units and packaged.

Benefits of Hot Rolled Steel

Hot rolled steel offers several manufacturing advantages, such as:

• Lower cost: Hot rolled steel tends to be less expensive than cold rolled steel since it involves less processing.
• Better workability: As the hot rolling process occurs at elevated temperatures, the processed material is easy to form and shape.
• Little to no internal stress: The hot rolling process involves cooling the steel gradually, which allows the material to essentially normalize its structure and become free of internal stresses.

Applications of Hot Rolled Steel

Since hot rolled steel shrinks slightly during the cooling stage, there is a lesser degree of control over its final shape. For this reason, it is typically used in applications that do not require extremely tight tolerances, such as:

• Agricultural equipment
• Automobile parts (e.g., frames and wheel rims)
• Construction materials (e.g., I-beams)
• Railroad equipment (e.g., tracks and railcar components)